Ruthenium Oxide Nanotubes Via Template Electrosynthesis

Carmelo Sunseri, Rosalinda Inguanta, Patrizia Livreri, Salvatore Piazza, Germano Ferrara, Rosalinda Inguanta, Germano Ferrara, Carmelo Sunseri, Salvatore Piazza

Risultato della ricerca: Articlepeer review

11 Citazioni (Scopus)


Ruthenium oxide nanotubes were fabricated by a single-step galvanostatic deposition using porous anodic alumina membraneas template. For the electrodeposition process, we used a electrochemical cell specifically designed in order to employ only 0.5 ml of 0.02M RuCl3•xH2O solution. The deposition from a very small volume was specifically addressed owing to the high cost of ruthenium compounds,which could be of some relevance from an applicative point of view. Several techniques were used to characterize the samplesprior to and after thermal treatment, which was carried out at different temperatures in order to study the crystallization process of the deposit.Raman spectroscopy of as-deposited nanotubes revealed the presence of RuO2 vibrating modes, while XRD patterns did not showRuO2 peaks, consequently the formation of a subnano-crystalline structure was proposed. After thermal treatment at different temperatureabove 600°C, they crystallized in the tetragonal form of RuO2. Both XRD analysis and Raman spectroscopy revealed that crystal size ofthe deposit grew with temperature up to 1000°C. SEM investigations showed the formation of nanotubes having an uniform average externaldiameter, while wall thickness changed throughout the height.
Lingua originaleEnglish
pagine (da-a)210-218
Numero di pagine9
RivistaCurrent Nanoscience
Stato di pubblicazionePublished - 2011

All Science Journal Classification (ASJC) codes

  • ???subjectarea.asjc.1300.1305???
  • ???subjectarea.asjc.1500.1502???
  • ???subjectarea.asjc.2700.2701???
  • ???subjectarea.asjc.2200.2204???
  • ???subjectarea.asjc.3000.3003???


Entra nei temi di ricerca di 'Ruthenium Oxide Nanotubes Via Template Electrosynthesis'. Insieme formano una fingerprint unica.

Cita questo