Polymer-modified bitumen (PMB) is bitumen that has been specifically engineered with polymer for providing enhanced performance in service. The aging of bitumen is a main aspect that is able to affect its final performance: during the production phase in a hot mix plant, all the binders experience short-term aging due to the high processing temperature. The same is true during the production of the modified binder, when the polymer is dispersed at high temperature in the bitumen mass. This paper aims at studying the effect of short-term aging when using different types of modifiers such as recycled polymers obtained from waste materials. A 50/70 penetration-grade bitumen has been modified, and bitumen characterization has been carried out before and after short-term aging; conventional tests, viscosity measurements, and dynamical mechanical analysis have been used to investigate the properties. Different aging indices have been determined for predicting the effect of short-term aging based on the type of modifier. Furthermore, the morphology of the modified bitumen has been investigated via fluorescent microscopy, before and after aging, in order to highlight morphological changes due to aging. The results confirm that aging affects all the modified binders, due to the thermal stress imposed during PMBs production. Nevertheless, polymer modification is proved to reduce the aging effect in terms of an increase in the elastic modulus as experienced by the original binder.
|Numero di pagine||21|
|Stato di pubblicazione||Published - 2020|
All Science Journal Classification (ASJC) codes
- Polymers and Plastics