Effects of anodizing surface treatment on the mechanical strength of aluminum alloy 5083 to fibre reinforced composites adhesive joints

Risultato della ricerca: Articlepeer review

Abstract

In this study, the anodizing process based on the use of tartaric sulfuric acid solution (TSA) was carried out on metal substrate to evaluate for the first time its effect on the adhesion strength and corrosion resistance of aluminium alloy (i.e., AA5083) to fibre (i.e., basalt or glass) reinforced composite adhesive joints for nautical applications. Furthermore, some TSA anodized samples were soaked in a NaOH solution to investigate the influence of this post-immersion step on the joint performances. With the aim to improve the fibre-matrix adhesion in the composite substrate thus further increasing the overall mechanical response of the joint, glass and basalt fibres were treated with a silane coupling agent solution. The corrosion behaviour of the aluminium alloy was studied by electrochemical techniques. Samples morphology was analysed by scanning electron microscopy, while the interaction between aluminium alloy substrate and epoxy resin was studied through contact angle analysis and resin uptake tests. The effectiveness of the silane treatment was examined by means of Fourier transform infrared spectroscopy and quasi-static tensile tests carried out on dry glass and basalt fabrics. The mechanical response of the resulting joints was evaluated by means of quasi-static tensile tests in accordance to ASTM D3528 standard.
Lingua originaleEnglish
pagine (da-a)1-10
Numero di pagine10
RivistaInternational Journal of Adhesion and Adhesives
Volume108
Stato di pubblicazionePublished - 2021

All Science Journal Classification (ASJC) codes

  • ???subjectarea.asjc.2500.2502???
  • ???subjectarea.asjc.1500.1500???
  • ???subjectarea.asjc.2500.2507???

Fingerprint

Entra nei temi di ricerca di 'Effects of anodizing surface treatment on the mechanical strength of aluminum alloy 5083 to fibre reinforced composites adhesive joints'. Insieme formano una fingerprint unica.

Cita questo