Effect of preparation method on the properties of poly(methyl methacrylate)/mesoporous silica composites

Francesco Armetta, Maria Luisa Saladino, Motshabi A. Sibeko, Luyt, Alberto Spinella

Risultato della ricerca: Articlepeer review

1 Citazioni (Scopus)

Abstract

The preparation method of a polymer composite and the filler loading are amongst the factors that influence the properties of the final composites. This article studies the effect of these factors on the thermal stability and thermal degradation kinetics of poly(methyl methacrylate) (PMMA)/mesoporous silica (MCM-41) composites filled with small amounts of MCM-41. The PMMA/MCM-41 composites were prepared through in situ polymerisation and melt mixing methods, with MCM-41 loadings of 0.1, 0.3, and 0.5 wt.%. The presence of MCM-41 increased the thermal stability of PMMA/MCM-41 composites prepared by melt mixing, but in the case of the in situ polymerised samples, the MCM-41 accelerated the degradation of the polymer. As a result, the activation energy was low and less energy was required to initiate and propagate the degradation process of these composites. The small-angle X-ray scattering (SAXS) measurements showed that the preparation method of the composites had no influence on the pore size of MCM-41, but the PMMAs used in the two methods both had shorter chains than the MCM-41 pore size. This allowed the polymer chains to be trapped inside the pores of the filler and be immobilised, as was observed from nuclear magnetic resonance (NMR) spectroscopy. The immobilisation of the polymer chains was more significant in the in situ polymerised samples.
Lingua originaleEnglish
pagine (da-a)363-370
Numero di pagine8
RivistaEMERGENT MATERIALS
Volume2
Stato di pubblicazionePublished - 2019

All Science Journal Classification (ASJC) codes

  • Biomaterials
  • Renewable Energy, Sustainability and the Environment
  • Waste Management and Disposal
  • Ceramics and Composites

Fingerprint Entra nei temi di ricerca di 'Effect of preparation method on the properties of poly(methyl methacrylate)/mesoporous silica composites'. Insieme formano una fingerprint unica.

Cita questo