Ce0.8Sm0.2O2Â âÂ xpowders were synthesized by solution combustion synthesis using citric acid, cellulose and sucrose as single, or intimately mixed, fuels. The powders were characterized by X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, N2sorption at â196Â Â°C, H2-temperature programmed reduction and thermogravimetric analyses. Textural properties of the powders were shaped by the peculiar employed fuel. The study of reducibility revealed that oxygen vacancies formation is mainly influenced by both parameters, specific surface area and total pore volume. The different tendency toward reduction played a key role in sintering under reducing atmosphere (4% H2/Ar), and Ce0.8Sm0.2O2Â âÂ xprepared with sucrose showed, at scanning electron microscopy images, the highest average grain size. Impedance spectroscopy experiments in air disclosed different grain boundary resistances on the basis of synthesis fuel employed and, in particular, Ce0.8Sm0.2O2Â âÂ xprepared with sucrose exhibited the best electrical performance. Solution combustion synthesis thereby was able to tailor the morphological and reduction properties of Ce0.8Sm0.2O2Â âÂ xpowders affecting even the microstructure of sintered pellet.
|Numero di pagine||9|
|Rivista||APPLIED CATALYSIS. B, ENVIRONMENTAL|
|Stato di pubblicazione||Published - 2016|
All Science Journal Classification (ASJC) codes
- Environmental Science(all)
- Process Chemistry and Technology
Aliotta, C., Martorana, A., Deganello, Muccillo, La Parola, V., Muccillo, Liotta, L. F., Deganello, F., Liotta, L. F., & La Parola, V. (2016). Ceria-based electrolytes prepared by solution combustion synthesis: The role of fuel on the materials properties. APPLIED CATALYSIS. B, ENVIRONMENTAL, 197, 14-22.